Quantcast
AR15 trigger polishing question - THR
THR  

Go Back   THR > Ammunition, Gear, and Firearm Help > Gunsmithing and Repairs

Welcome to THR
You are currently viewing our site as a guest which gives you limited access to view most discussions, articles and access our other FREE features. By joining our free community you will have, access to post topics, communicate privately with other members (PM), respond to polls, and access many other special features. Registration is fast, simple and absolutely free so please, join our community today!


If you have any problems with the registration process or your account login, please visit the help section.

Reply
 
Thread Tools
Old August 7, 2014, 11:50 AM   #1
thefish
Member
 
 
Join Date: February 17, 2012
Location: Colorado
Posts: 456
AR15 trigger polishing question

So I read a few threads about taking the grit out of the AR15 trigger, and polishing the sear face on the trigger and hammer seemed like the ticket.

One thing I did make note of was the warning not to remove any metal as the case hardening is very thin.

Some guys recommended polishing compound, others sandpaper. So I gave it a shot with Brasso and the Dremel. Well, after 30 minutes or so, the results were not happening, so I did some light polishing with 600 grit sandpaper.

And I mean real light, there was no metal material on the sandpaper whatsoever, just slight discoloration. The face really seems to begin shining the mirror finish I was looking for, however, it seems uneven. The center of the face hasn't started to polish up yet, but the edges are nice and shiny.

My question is, should I keep going? I don't really know how thick the case hardening is, and don't want to ruin it. I understand the engagement area is very small and only at the top, so I wont polish the whole face, just the top 1/3rd.

I was kind of surprised the Brasso and dremel didn't have much effect, but the 600 grit did.

Pics attached.

Thanks in advance.
Attached Images
File Type: jpg DSC_8417.JPG (186.4 KB, 29 views)
File Type: jpg DSC_8421.jpg (66.1 KB, 27 views)
File Type: jpg DSC_8424.jpg (49.1 KB, 29 views)
thefish is offline  
Old August 7, 2014, 12:03 PM   #2
loose noose
Member
 
 
Join Date: February 22, 2012
Location: Southern Nevada
Posts: 1,810
fish what brand of AR-15 is it?
loose noose is offline  
Old August 7, 2014, 12:25 PM   #3
thefish
Member
 
 
Join Date: February 17, 2012
Location: Colorado
Posts: 456
This is actually just a trigger from Palmetto state. If I recall, its the Ptac trigger kit, in an Anderson lower.

I was going to experiment with this one, and if it goes well, polish the trigger on my M&P15T and my other PSA build (Anderson lower, PSA premium FCG, PSA premium upper with SS barrel, Magpul MOE stock), and add the JE enterprises yellow spring kit I have on order.
thefish is offline  
Old August 7, 2014, 04:54 PM   #4
Louca
Member
 
 
Join Date: August 29, 2013
Location: Michigan
Posts: 141
Nice pics fish. They tell a lot. The likely reason the polishing is not smooth all the way across is probably because you are are either moving the sear and/or the sandpaper off perfectly flat as you polish. Same thing would happen to me (when I used to polish AR sears). I no longer do that since I have no idea how thick the hardness is on those sears. You may have read my post on the subject here.

But, I would argue that if the hardness is super thin, it will wear off over time anyway as the trigger is used. Cheap components are cheap and it might be tough to make them any good.

Back to your polishing, on stock ARs, the hammer appears to be "cocked" further as the trigger is pulled. I am quite sure that is done for safety and itself is a huge contributor to the pull force necessary to disengage the trigger. Because of that action (sear angle actually), just the very edge of the hammer sear rides or scrapes along a longer portion of the trigger sear. All this is to say is that from your pics you are polishing the most important sear, the trigger sear. The hammer sear should also be smooth, but the edge is the most important part of that sear. Well, also important is the sear edges also need to be perfectly parallel to their axes of rotation. I have seen a few that were not.

I like polishing and changing angles to tune triggers but I will no longer do it on ARs since the quality of the metal is unknown. If the metal quality was known, it may be possible to determine if the polished sears could be re-hardened to make that nice work last. With ARs I guess I will have to pay someone else to do that. What you are doing is interesting but dangerous - be careful.

Lou
Louca is offline  
Old August 7, 2014, 05:03 PM   #5
HRnightmare
Member
 
 
Join Date: July 30, 2014
Posts: 187
I literally bought hundreds of the PTAC lower parts kits. I am not exaggerating, probably about 250ish when they were $29.99 at PSA

Some of them were awesome and some of them felt like there was sand in the trigger assembly.

I took a cloth polishing tip for my dremel and some Flitz jewelers polish, rubbed it by hand on the trigger and hammer and lightly hit it with my dremel on a slow-medium speed. Than use a soft cloth with lubircating oil to wipe any excess paste away.

After that nearly all of them were noticeable better. A handful of them were still garbage. One was TERRIBLE. I emailed PSA about it and they actually sent me a PSA branded replacement trigger assembly kit.

Last edited by HRnightmare; August 7, 2014 at 05:10 PM.
HRnightmare is offline  
Old August 7, 2014, 05:10 PM   #6
HRnightmare
Member
 
 
Join Date: July 30, 2014
Posts: 187
Not to be offensive but if you want a smooth trigger I would suggest going with a higher quality trigger kit, maybe even an enhanced trigger kit Recoil did an awesome comparion of like 12 of them. Everything from the Geisselle to the Spikes to cheap ones that are only like $50. You likely won't see a ton of improvement since like others have said, part of the issue might be the metal quality as much as the smoothness and angle, etc.



I just recently upgraded to a nickel boron coated trigger kit and BCG on my SBR because of the amount of gas blowback, especially suppressed. The difference between that and the standard (Magnesium Phosphate???) metal is certainly noticeable.
HRnightmare is offline  
Old August 7, 2014, 05:22 PM   #7
Drail
Member
 
 
Join Date: January 17, 2008
Posts: 3,589
Use a stone, not a Dremel for that kind of work. You simply rounded off the edges. The bearing surface needs to be even all the way across and square to the sear. If you don't have the tools or the knowledge it's better to leave it alone.
Drail is offline  
Old August 7, 2014, 06:19 PM   #8
BBBBill
Member
 
 
Join Date: March 7, 2005
Location: Florida
Posts: 1,364
Original AR-15/M-16 fire control parts were reportedly made of sintered steel. Not the best stuff for trying to get a decent trigger pull. No one with much experience will touch them anymore due to the variable case hardening. The over-cock described above is critical for most self loading firearms to keep the hammer from falling as the bolt slams home if the trigger is tuned. The vibration is strong enough to overcome spring pressure and make the hammer slip off the sear when engagement surfaces are altered. With the AR it is far better to bite the bullet and spend your money on a quality unit like Timney, Wilson, or Geissele. Steer clear of Rock River. They don't stand behind their triggers. Not usually a problem and the trigger pull is pretty nice, but when the hammer breaks for no reason, you want the manufacturer to step up.
BBBBill is offline  
Old August 7, 2014, 06:57 PM   #9
carbine85
Member
 
 
Join Date: July 1, 2007
Location: Southwest, Ohio
Posts: 1,333
Slowly polish it with a polishing compound or a stone. Check the pull as you.
If you do upgrade the trigger the Rock River is GTG. I have 4 and never had an issue. I would bet I have 20,000 round down range between all of them
__________________

"That's the good thing as a President, I can do whatever I want"
Barack Obama - Americas 1st Dictator
"I ask sir, what is the militia? It is the whole people except for a few politicians."
George Mason (father of the Bill of Rights)
carbine85 is offline  
Old August 7, 2014, 07:44 PM   #10
BBBBill
Member
 
 
Join Date: March 7, 2005
Location: Florida
Posts: 1,364
..and I know of 3 Rock River hammers that broke within a year. All were owned by different members of my former shooting club. Rock River would not even offer a discount on replacement. Since I sold one of them through my shop, I ate the cost of the parts so the shooter could get a new trigger group.
BBBBill is offline  
Old August 7, 2014, 07:51 PM   #11
rcmodel
Contributing Member
 
 
Join Date: September 17, 2007
Location: Eastern KS
Posts: 49,374
The edges are rounded because you are rocking it on the sandpaper.
Or using a soft backing behind the sandpaper?

Whichever, you are doing more harm then good.

rc
__________________
Don't put all your eggs in one basket.
Or all your primers in a glass jar!
rcmodel is offline  
Old August 7, 2014, 11:08 PM   #12
thefish
Member
 
 
Join Date: February 17, 2012
Location: Colorado
Posts: 456
Hi Guys, thanks for the replies. I'm using a flat piece of glass under the sandpaper, and although in the pics the edges look rounded, they aren't. it's a combination of the lighting, and the lense I have has a ridiculous amount of lack of depth of field (105mm micro-nikor) so it's hard to get a pic that's sharp all the way through. Another is attached. To the naked eye, with a magnifying glass, the edges are all sharp and the same profile where the hammer actually engages the small edge.

At some point I'll look at possibly a trigger upgrade, just wanted to make this one a little better. In any event, it's an easily replaceable part. With this but of polishing, the grit is gone and it feels a million times better.

Thanks again!
Attached Images
File Type: jpg DSC_8445.jpg (34.8 KB, 29 views)
thefish is offline  
Old August 8, 2014, 11:10 AM   #13
HRnightmare
Member
 
 
Join Date: July 30, 2014
Posts: 187
I have never had to deal with Rock River but I own two of their rifles and LOVE them. I agree that there Std trigger kits are awesome. Hell I think there stock trigger kit was better than the upgraded premium Spikes kit I bought and then quickly resold.
HRnightmare is offline  
Old August 10, 2014, 12:52 AM   #14
cheep
Member
 
 
Join Date: August 22, 2011
Posts: 19
Don't be afraid to work on an AR trigger as they are cheap enough to replace if it doesn't work out. Use a stone and then polish for a better feel but keep edges sharp and surfaces flat.
cheep is offline  
Old August 10, 2014, 01:04 AM   #15
zoom6zoom
Member
 
 
Join Date: April 24, 2006
Location: Virginia
Posts: 2,804
1. Go slow. No, slower.
2. No power tools. You're trying to polish, not remove metal. Use a stone.
3. Do not change geometry / break or round over any edges.
4. Reassemble and test frequently.

Honestly, the easiest way is to dry-fire the snot out of it. Or just get a Geissele... you'll want to eventually anyway.
__________________
www.vcdl.org Certified AR15/M16 and SIG pistol armorer.
zoom6zoom is offline  
Old August 10, 2014, 09:35 AM   #16
cbob1911
Member
 
 
Join Date: August 18, 2012
Posts: 8
polished mine w/ fritz, bobbed the hammer, installed pre-travel set screw, and JP yellow springs. It's comparable to other high end drop-in triggers i have.
cbob1911 is offline  
Reply


Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -4. The time now is 06:04 PM.


Powered by vBulletin® Version 3.8.6
Copyright ©2000 - 2014, Jelsoft Enterprises Ltd.
vBulletin Optimisation by vB Optimise.
This site, its contents, Shooting Reviews, and its contents are Copyright (c) 2010-2013 Firearms Forum, Inc.
IMPORTANT DISCLAIMER
Although The High Road has attempted to provide accurate information on the forum, The High Road assumes no responsibility for the accuracy of the information. All information is provided "as is" with all faults without warranty of any kind, either express or implied. Neither The High Road nor any of its directors, members, managers, employees, agents, vendors, or suppliers will be liable for any direct, indirect, general, bodily injury, compensatory, special, punitive, consequential, or incidental damages including, without limitation, lost profits or revenues, costs of replacement goods, loss or damage to data arising out of the use or inability to use this forum or any services associated with this forum, or damages from the use of or reliance on the information present on this forum, even if you have been advised of the possibility of such damages.