Load Data for lead bullets

Discussion in 'Handloading and Reloading' started by smaj100, Jun 6, 2009.

Thread Status:
Not open for further replies.
  1. smaj100

    smaj100 Member

    Joined:
    Mar 5, 2009
    Messages:
    7
    Location:
    Alabama
    Hi all,

    With reloading equipment so hard to come by these days, I want to start casting bullets for my wifes 380. I have several reloading manuals and the lyman 49th allows for 120gr lead with appropriate powder data.

    My question is has anyone used anything heavier than that? I am specifically wondering if my 125gr 9mm bullet will work? If it will do I drop the powder down and start over at 3.5gr Win231? I have a Lee TL356-125gr 6 cavity that I want to use.

    I love the lee tumble lube on my 40 and 308 so I am hoping it will work. Thanks in advance for any help yall can provide.

    Update..
    That was a typo on the load data 2.1gr it was it should have read. I am not looking for stellar performance or crazy knock down power. I reload that thing so my wife can shoot regularly without breaking the piggy bank. I haven't been able to get my hands on a 100gr 356 mold so I wondered to myself if my 125gr 9mm mold would do the trick. Not wanting to scare or hurt my wife I figured I would ask the question before I started stuffing big heavy bullets in that tiny case and pulling the trigger.
     
    Last edited: Jun 6, 2009
  2. Claude Clay

    Claude Clay Member

    Joined:
    Mar 6, 2007
    Messages:
    2,700
    Location:
    CT
  3. Randy1911

    Randy1911 Member

    Joined:
    Mar 15, 2009
    Messages:
    914
    Location:
    Arkansas
    You might find the data here. http://data.hodgdon.com/main_menu.asp

    Where are you getting your data from. My Lyman Pistol and Revolver Handbook show that 3.5 with a 90 gr. bullet is max. With a 120 gr. bullet it shows a max of 3.2 grs.
     
  4. The Wiry Irishman

    The Wiry Irishman Member

    Joined:
    May 22, 2006
    Messages:
    1,178
    Location:
    West Lafayette, Indiana
    .380s have a lot less bullet sticking out the case than 9mm, I'm not sure you could fit a 9mm bullet in a .380 magazine.
     
  5. ArchAngelCD

    ArchAngelCD Member

    Joined:
    Nov 25, 2006
    Messages:
    22,095
    Location:
    Northeast PA, USA
    A 120gr bullet is very heavy for a .380 Auto. even if you could get it to fit in the Mag what performance could you expect? You might end up with a bullet stuck in the barrel.
     
  6. MMCSRET

    MMCSRET Member

    Joined:
    Feb 18, 2008
    Messages:
    2,971
    Location:
    North Central Montana, across the Wide Missouri
    The heaviest bullet I have had success with in cast for 380 Auto was 100 gr. Any heavier and you get overwhelmed by the "Law of Diminishing Returns"
     
  7. 243winxb

    243winxb Member

    Joined:
    Jul 7, 2004
    Messages:
    8,993
    Location:
    USA
    My guess is- your Lee 125gr bullet should work fine in the 380. My old lyman 45 edition list the lyman 121 gr.#358242 bullet, a round nose, with 2 grease grooves. Your Lee shows only 1 grease grove. With 1 less groove, i would think your Lee bullet is shorter in OAL , but not my much, if any. Just a Guess remember. One problem i see is, as with all cast bullet, the alloy used, the as cast bullet will not weight 125gr. I will be much heavyer. Reduce your load accordingly. Linotype would give a less heavy bullet. Starting load of 1.6 gr Bullseye @661 fps should get the bullet out the barrel. Unique looks like a better choice of powders. Starting load of 3.5gr Unique with the 121gr listed gave 939 fps.. I do NOT load 380auto.
     
  8. rcmodel

    rcmodel Member in memoriam

    Joined:
    Sep 17, 2007
    Messages:
    59,082
    Location:
    Eastern KS
    The only problem, if there is one, will be severe case bulge at the base of the longer bullet.
    That may or may not cause chambering issues.

    The case-wall taper makes the case thicker further down.
    In the .380, the taper ends about where the base of a 90 - 100 grain bullet will be when loaded to SAAMI max OAL of .984".

    rc
     
  9. Marlin 45 carbine

    Marlin 45 carbine Member

    Joined:
    Jul 15, 2007
    Messages:
    2,477
    Location:
    South-Western North Carolina
    I bought some very good shooting cast .380 slugs from Mike at 'mastercastbullets.com' around 95gr IIRC. shoot as good if not better than the hi$ Speer fmj and Rem hp I was loading.
    over Red Dot or BullsEye.
     
  10. jfdavis58

    jfdavis58 Member

    Joined:
    Jul 19, 2007
    Messages:
    303
    Location:
    Albuquerque (NE heights), NM