nice, wish i could take mine from my phone there almost one hole 3 and 4 shot group in the rain

just bought a FNAR heavy Barrel, I shot sub moa at 100 yards consistantly with a really cheap scope I thought would fall apart A BSA was 100 bucks. I really thought i wanted a LR 308 DPMS but if you go to their forum you will find nothing but problems the my dealer let me shoot the one I...

GREAT, that is what I want going to buy some now then going to the range and shoot for a while

55 gr montana gold, accuracy was great, you load H335? I am told I will get more uniform drops the 4198 was varying .6 of gr. or more I am used to being on the money all the time, the shape of 4198 is what the problem is.

They will only be used in one gun my new AR 15 by Stag left handed, my first few i loaded cycled and ran flawless, did those on single stage I should have my shell plate Monday to load on my Hornady progressive press, I also bought a Lee case activated powder measure, changeing my hornady from...

Thanks, that is what I thought.

I have been reloading pistol straight wall cases and casting for many years but never rifle, so when and why would you only size the neck instead of the whole cases that also does neck, I bought the lee deluxe 3 die set, I see no reasonfor just neck sizing, doing .223

I quit useing unique it varies to much

yes that will eliminate any more guess work about the hardness

oops i forgot to go up and read a post telling you to double lube so you did that ? now add some hardenner lino or pure antimony, I will just assume your to soft so if you get pure antimony add 3/4 of a pound to ten pounds of what your useing if you cant get antimony then go to ebay for lino...

Save some time go to Brownells and get the Lewis Lead remover I don't remember but I think $25 or so you will have it clean in 10 minutes, I have never had one lead at the muzzle bu it can't hurt to add some antimony or lino type if you have it, some how I think you could be to soft, but lube...

okay did you shoot a hundred? and after you rana brush down the bore did it clean up? if it cleaned up after 100 rounds and no build up and you did not spend hours cleaning it you could be ok, most leading occurs just a inch past chamber you said at end of barrel, right?

bullseye, sounds like your good to go, if you have no leading your good as far as dropping in water I been doing that 20 years so I disagree with 243win and if you talk to Lee or Lyman they will tell you it does harden them and like I said been doing that long time never any leading I shoot my 9...

have you even tried shooting any of those at .355 or .356 if not shoot them your barrel should be .355 and either should really be ok

One more thing Lee molds cast light if using Lyman #2 mix they test their weight at a 20 to 1 mix, in other words the same mix in a Lyman mold will be on the money weight wise in a Lee mold it will be light by 2 gr. on a 9mm and about 3 to 4 on a 45, I got that info from Lee, long time ago Pat...

243win, never heard of such a thing, anything can happen but more lead the heavier the bullet will be but it should not be smaller if the mold is full but like I said anything can happen bullseye I have never been to crazy about lee molds I may have that mold from when I first started but I...

he said he is using WW wheel weights that have antimony there should be no problem with the tin that should be 1/2 pound per 9 pounds of WW for a lyman #2 mix and I have never seen any shrink when drop in water and I been dropping them along time that will only harden them according to support...

just melt them back down, its not like they will ever get to hard like a jacket with that mixture

That is a good thing just adj the extractor

I had that problem with a SA, try something get all the ammo you plan to shoot take the barrel out and put each round in the chamber they should drop in very easy and fall out if they don't then the chamber needs to be reamed I had this issue with SA if they do fall out then extractor