At those velocities, you shouldn't have a leading problem, if your using a good lube on them. Leave the hard cast bullets in the mix to keep the hard alloy qualities and molten metal flow qualities. If you still have concern about hardness, just add some used wheel weights to the mix, while your refining into ingots. A local tire dealer should be able to supply those fairly cheap.