Most of them are made of antimonous lead alloy. (not sure if I spelled that right.) A few are made of iron, and a few are made of zinc. The lead ones make very good bullets as long as you don't contaminate them with zinc when you melt them down in to ingots.
I drop my bullets from the mold into a pan of water to harden them somewhat. If you heat wheelweight alloy to just below the slump point and quench in water, the bullets can achieve a hardness of over 30 BNH. (I'm not heat treating mine to anywhere near that hardness)
Wheel weights make good bullets for pistols . Drop them from the mould into a bucket of water... makes them harder Be careful not to let water splash in the lead pot. I make all my pistol bullets out of wheel weights. I keep my loads below 1000fps. Most of my loads are for target pratice or plinking. I get little or no leading at these velocities.
lead melts at app. 650f &zinc at app 1000f.
hold the smelting temp down & skim it out with the other dross!!!
go visit castboolits.com & search ,very much reading on the subject of zinc!!!!
oh almost forgot: WW are probably too hard for BP shooting ,youll need to seperate the (stick ons) from the (clip ons) generally softer.
most clipons will give you an alloy of 14- 19 bhn,BP needs 5-8 bhn to arbitrate in the barrel under pressure.
The lead tape weights are pure lead. Pure lead is much sought-after by black powder shooters. Clip on weights are alloyed with antimony and usually a little tin and arsenic, to make the metal harder. It is a favorite of smokeless powder pistol shooters.
Then there is type-metal, which is very hard eutectic alloys that contains significant amounts of tin and a huge amount of antimony. Type-metal, especially linotype, is much sought after by rifle shooters.
Unless you are smelting over a turkey burner, the zinc weights will float to the top long before they melt. Just don't leave the pot unattended when smelting. You're going to have to skim off the clips and dross anyway, so it's not a big deal. Just skim as soon as the stuff melts, and you have no worries re zinc weights. Iron weights and steel clips also float to the top.
The other trick that'll help you is to leave a couple of inches of lead in your smelting pot after you're done the first time. The next time it will melt faster and give the "new" clips something to float on and make your skimming easier.